– Investigation of Mechanical Properties of Zeolite-Y and Zsm-5 Catalysts Synthesized from Locally Available Clays – 

Download Investigation of Mechanical Properties of Zeolite-Y and Zsm-5 Catalysts Synthesized from Locally Available Clays project materials: This project material is ready for students who are in need of it to aid their research.

ABSTRACT

This research work was centred on and ZSM-5 catalysts synthesized from locally available clays such as Kaolin, Alumina, Gambe and Pindiga respectively. Pressure absorption capacities of the synthesised zeolite catalysts and that of the supportive clays were carried out with the aid of a bourdon gauge machine.

alongside with a micro tensometer machine were equally used to determine the young’s modulus of the synthesized zeolite catalysts and flow characteristics of the clays. XRD analysis was carried out using Cu K α-radiation to find the textural properties.

Results of the analysis  indicated that synthesised ZSM-5 catalyst was denser, could absorbed more pressure as compared with synthesized Zeolite-Y catalyst. Though, in terms of flowability, synthesised Zeolite-Y is more effective than synthesise ZSM-5 catalyst.

The young’s modulus of the synthesised catalysts was found to lie between 3.5 N/mm2 – 4.0 N/mm2. Among the clays analysed, alumina clay had proved a more superior support material for the synthesis of the zeolite catalysts in terms of flowability, porosity, and pore size.

XRD analysis indicated that at point 2-theta (point where the highest peak occurred), the peak level of the synthesized zeolite catalysts and that of the referenced zeolite are, at the same level which indicated similarity in their performance ability.

TABLE OF CONTENTS

Title page- i

Declaration- ii

Certification– iii

Acknowledgement iv

Abstract—– v

Table of Contents– vi

List of Tables—- xi

List Figures– xi

List of Plates— xii

CHAPTER ONE: INTRODUCTION

  • Background to the study- 1
  • Statement of the problem– 4
  • The present research- 4
  • Aim and Objectives- 5
    • Aim 5
    • Specific Objectives- 5
  • Significance of study- 5
  • Justification– 6
  • Scope of study 6
  • Limitation— 6

CHAPTER TWO: LITERATURE REVIEW

  • Introduction– 7
  • Properties of Zeolite 8
  • Catalysts— 10
  • Catalytic Cracking– 11
  • Uses of Zeolites— 12
    • Commercial and domestic uses 12
    • Petrochemical industry- 12
    • Nuclear industry 13
    • Heating and Refrigeration–13
    • Construction-13
  • Review of past work— 14
  • Catalyst support— 17
  • Supported catalyst- 18
  • Uses of kaolin clay- 19
  • Compaction and Mechanical properties- 21

CHAPTER THREE: MATERIALS AND METHODS

Materials, Equipment and Methods– 23

Materials- 23

Equipment—- 24

  • Methods and experimental procedures- 24
  • Uniaxial compression test—- 24
  • Flow characteristics– 26
  • Stress-Strain Analysis—– 27
  • X-ray diffractometer analysis– 27

CHAPTER FOUR: RESULTS AND DISCUSSIONS

Results and Discussions- 28

Results-28

  • Compressive pressure absorption of Kaolin Zeolite-Y, ZSM-5 and Alumina clay- 28
  • Stress / Strain Analysis on Gambe clay, Pindiga clay and Kaoli clay- 30
  • Stress / Strain Analysis on Sample A and Sample B- 31
  • Compression test on zeolite-Yn, gambe clay and pindiga clay32
  • Analytical Comparison between CPD commercial Zeolite-Y, CPD pure chemical ZSM-5 and CPD ZSM-5 ϓ alumina33
  • Comparison of compressive pressure against Load for Zeolite-Yn, Zeolite-Ys and Compounded commercial Zeolite-Y34
  • Pressure absorption comparison between Gambe clay, Pindiga clay, Kaolin and Alumina clay– 35
  • Pressure absorption capacity of Synthesized ZSM-5, pure chemicalnZSM-5 and Compounded ZSM-5 γ alumina- 36
  • Stress / Strain Analysis on Zeolite-Yn– 37
  • X-ray diffractometer (XRD) analyses 38

Discussion of Results- 41

  • Discussion on compressive pressure absorption of kaolin clay, zeolite-Y, ZSM-5 and alumina clay41
  • Discussion on stress / strain analysis on gambe clay, pindiga clay and kaolin clay– 42
  • : Discussion on stress / strain analysis on sample A and sample B— 42
  • Discussion on compression test on zeolite-Yn, Gambe clay and Pindiga clay— 44
  • Discussion on Analytical Comparison between CPD commercial Zeolite-Y, CPD pure chemical ZSM-5 and CPD ZSM-5 ϓ alumina-44
  • Discussion on Comparison of compressive pressure against Load for Zeolite-Yn Zeolite-Ys and Compounded commercial Zeolite-Y– 44
  • : Discussion on Pressure absorption comparison between Gambe clay, Pindiga clay, Kaolin and Alumina clay45
  • Discussion on Pressure absorption capacity of Synthesized ZSM-5, pure chemical ZSM-5 and Compounded ZSM-5 γ alumina- 45
  • Discussion on Stress / Strain Analysis on Zeolite-Yn— 46
  • Discussion on X-ray diffractometer (XRD) analyses—– 46

CHAPTER FIVE: CONCLUSIONS AND RECOMMENDATIONS

Conclusions and Recommendations—– 48

Conclusions——— 48

Recommendations for Further Research Work—- 49

Contribution to Knowledge——— 49

References—- 50

INTRODUCTION

Zeolites are minerals used for numerous commercial and domestic applications. These include applications in petroleum and petrochemical industries as catalysts, adsorbents and ion exchangers, nuclear industries for nuclear reprocessing, heating and refrigeration, detergents, construction as material additives, medicine, agriculture as a soil treatment, gemstones, as ion-exchange beds in domestic and commercial water purification and softening.

The term Zeolite was originally coined in 1756 by Axel Fredrik Cronstedt, who observed that upon rapidly heating the material stilbite, it produced large amounts of steam from water that has been adsorbed by the material. Base on this, he called the material zeolite, from the Greekzep, meaning “to boil” And lithos meaning “stone” (Cejka et al, 2007).

Today, Zeolite-Y is used commercially as because of its high concentration of active acid sites, its high thermal stability and high size selectivity. Zeolite-Y is a synthetic analog to the and crystallizes with cubic symmetry. It has crystal sizes in the approximate range of 0.2-0.5µm and pore diameter of 7.4À. It thermally decomposes at 793oC (Htay et al, 2008).

REFERENCES

Ahmed, A.S., Salahudeen, N., Ajinomoh, C.S., Hamza, H., and Ohikere, A. (2012). Studies on mineral and chemical characteristics of Pindiga Betonitic clay, Petroleum Technology Development J, (ISSN 1595 – 9104) – 1.

Ahmed, M. A. A. (2007). Development of NiM-Zeolite – Based catalysts for hydrocracking gas oil, synthesis, characterization, activity and kinetics studies, a Phd thesis submited to University of Sain Malasia.

Akia, M., Alavi S. M. and Yan Z. (2011). Dehydrogenation catalysts of higher normal parafins on a nanocrystalline γ-Al2O3 Support, different impregnation sequences, Journal of petroleum and Gas Engineering 2 (3): 64-73

Alireza, B., Navid M. N. and Hassan M. (2011). The Overall effect of Nano clay on the physical mechanical properties of Epoxy Resin, World Academic of Science, Engineering and Technology 73, 2011.

Al–Rasheed, A., Holecek S., Prazak M. and Procio M. (1993). Powder Metallurgy rout in production of Aluminium alloy matrix particulate composite.

StudentsandScholarship Team.

By admin

Leave a Reply

Your email address will not be published. Required fields are marked *